- ASTM A178/ASME SA178
- China
- Stock
- Grade A,Grade C,Grade D
ASTM A178/A178M Standard Specification for Electric-Resistance-Welded Carbon Steel and Carbon-Manganese Steel Boiler and Superheater Tubes
ASTM A178 Electric-Resistance-Welded Steel Tubes
ASTM A178/A178M
Standard Specification for Electric-Resistance-Welded Carbon Steel and Carbon-Manganese Steel Boiler and Superheater Tubes
Main Grade
Grade A, C, or D,
ASTM A178 Grade C and D tubes are not suitable for safe-ending for forge welding.
The tubing sizes and thicknesses usually furnished to this specification are 1 ⁄ 2 to 5 in. [12.7 to 127 mm] in outside diameter and 0.035 to 0.360 in. [0.9 to 9.1 mm], inclusive, in minimum wall thickness. Tubing having other dimensions may be furnished, provided such tubes comply with all other requirements of this specification.
Manufacture
The steel for Grade D shall be killed.
Tubes shall be made by electric-resistance welding.
Heat Treatment
After welding, all tubes shall be heat treated at a temperature of 1650°F [900°C] or higher and followed by cooling in air or in the cooling chamber of a controlled-atmosphere furnace. Cold-drawn tubes shall be heat treated after the final cold-draw pass at a temperature of 1200°F[650°C] or higher.
Chemical Composition
The steel shall conform to the requirements as to chemical composition prescribed in Table 1.
When a grade is ordered under this specification, supplying an alloy grade that specifically requires the addition of any element other than those listed in Table 1 is not permitted.
| Element | Composition, % | ||
|
Grade A,Low-Carbon Steel |
Grade C, Medium- Carbon Steel |
Grade D, Carbon-Man- ganese Steel |
|
| Carbon | 0.06–0.18 | 0.35 max | 0.27 max |
| Manganese | 0.27–0.63 | 0.80 max | 1.00–1.50 |
| Phosphorus, max | 0.035 | 0.035 | 0.030 |
| Sulfur, max | 0.035 | 0.035 | 0.015 |
| Silicon | .... | .... | 0.10 min |
General Requirements
Material furnished under this specification shall conform to the applicable requirements of the current edition of SpecificationA 450/A 450M unless otherwise provided herein.
Tensile Requirements
Grade C and D tubes shall conform to the requirements as to tensile properties prescribed in Table 2.
| Grade C | Grade D | |
| Tensile strength, min, ksi [MPa] | 60 [415] | 70 [485] |
| Yield strength, min, ksi [MPa] | 37 [255] | 40 [275] |
| Elongation in 2 in. or 50 mm, min, % | 30 | 30 |
|
For longitudinal strip tests a deduction for each 1 ⁄ 32 -in. [0.8 mm] decrease in wall thickness below 5 ⁄ 16 in. [8 mm] from the basic minimum elongation of the following percentage points shall be made. |
1.50 A | 1.50 A |
NOTE 3—Explanatory Note—For purposes of design the following tensile properties may be assumed for Grade A tubes:
| Tensile strength, min, ksi [MPa] | 47 [325] |
| Yield Strength, min, ksi [MPa] | 26 [180] |
| Elongation in 2 in. or 50 mm, min, % | 35 |
Crush Test
When required by the purchaser, crushing tests shall be made on sections of tube 2 1 ⁄ 2 in. [63 mm] in length which shall stand crushing longitudinally without cracking, splitting, or opening at the weld, as follows:
| Wall Thickness of Tubes, in. [mm] | Height of Crushed Section, in. [mm] | |
| 0.135 [3.43] and under |
3 ⁄ 4 [19] or until outside folds are in contact |
Grade C and D Tubes |
| Over 0.135 [3.43] | 1 1 ⁄ 4 [32] | .... |
Mechanical Tests Required
Flattening Test:
Flange Test:
Crush Test
Tension Test
Reverse Flattening Test
Hydrostatic or Nondestructive Electric Test
Forming Operations
When inserted in the boiler, tubes shall withstand expanding and beading without showing cracks or flaws, or opening at the weld. When properly manipulated, superheater tubes shall withstand all forging, welding, and bending operations necessary for application without developing defects.
Product Marking
In addition to the marking prescribed in Specification A 450/A 450M, the letters “ERW” shall be legibly stenciled on each tube, or marked on a tag attached to the bundle or box in which the tubes are shipped.
The manufacturer’s name or symbol may be placed permanently on each tube by rolling or light stamping before normalizing. If a single stamp is placed on the tube by hand,this mark should not be less than 8 in. [200 mm] from one end of the tube.
Product key description, this is a very good product description, detailing our product use, product characteristics